Mastering the causes of deformation of the brick machine support plate can easily solve the deformation problem

Brick machine pallets are products that we often use in our daily lives, solving many of our problems. However, due to the high requirements of product use, improper operation can cause deformation of the pallets. So, how to solve this problem? Don't worry, our manufacturer has provided a brief summary of the causes and solutions for the deformation of brick machine pallets. Come and bookmark it now.

image.png

Due to the uneven moisture content caused by different conditions on both sides of the board, the brick machine pallet is prone to deformation. What are the reasons for the deformation of the brick machine pallet?

1、 Reason for warping

1. Improper adhesive ratio can easily cause deformation of the brick machine pallet. It is recommended that everyone strictly follow the standard ratio for the ratio.

2. Improper hot pressing conditions, if overheated, may cause relative damage to the product. If the hot pressing is insufficient and cannot reach the required temperature, then the task cannot be completed.

3. The non burning brick machine pallet glued on the surface and back is asymmetric, which can easily cause warping of the brick machine pallet. It is recommended that everyone be careful and careful when gluing.

4. The moisture content of the non fired brick machine pallet is high, and it shrinks when dry.

2、 Take measures

1. Reduce the amount of urea formaldehyde resin adhesive, make the adhesive layer soft, and improve the hot pressing conditions.

2. Stack horizontally after hot pressing And press the weight, with the fiber direction of the pallet parallel to the direction of the substrate with less shrinkage and swelling.

3. When pasting, try to squeeze the support plate of the unburned brick machine as tightly as possible, and slightly loosen the central part.

4. Reduce the moisture content of the pallet and make it uniform.

First, prepare the magnesite slurry by sequentially adding light burned powder, magnesium chloride, water, modifier, inorganic filler, and organic filler to the pallet; Then pour the magnesite slurry into the cleaned mold, add alkali resistant glass fiber cloth and bamboo grates layer by layer, place the mold on the molding machine, press it into shape, and wait for reaction curing, demolding and curing until the age is reached. This product has the characteristics of high strength, resistance to cooking, impact, earthquake resistance, non water absorption, no deformation, no cracking, no pollution, long service life, and can be recycled and reused. Greatly reducing the production cost of bricks and solving the long-standing problem of new building materials factories